Method for packaging a liquid food product

ABSTRACT

The invention relates to a method of, and a device for delivering a predetermined ( 1 ) volume of beverage into a thermoplastic container formed from a heated preform, the preform being positioned in a mold, characterized in that the method includes a step of injecting at least some beverage into a recess in the preform so as to promote expansion of the preform inside the mold, the mold defining the shape of the container, a longitudinal displacement of a stretch rod ( 10 ) carried out during a given period ensuring longitudinal elongation of the heated preform, the stretch rod being immobile at the end of the given period, and a volume of beverage greater than a predefined fraction of the predetermined volume, preferably equal to 50%, being present in the recess at said end of the given period.

FIELD OF THE INVENTION

The present invention relates to the field of manufacturing containers made of a polymer material, especially a polyester. More particularly, it relates to the field of manufacturing polyester bottles, preferably polyethylene terephthalate (PET) bottles containing a liquid, preferably water and especially mineral water.

BACKGROUND OF THE INVENTION

For many years, the PET bottles usually found on the market have been manufactured by the blow moulding or stretch-blow moulding of PET preforms using compressed air.

A preform usually takes the form of a cylindrical tube closed at one of its ends and open at its opposite end. The open head of the preform corresponds to the neck of the container. During the conventional process for manufacturing containers from preforms, the preforms are slipped onto the cylindrical mounts of a continuous conveyor chain, which thus transports the preforms through an oven, essentially formed by a straight section bordered on each side by radiative heating means, so as to temperature-condition the plastic for the subsequent stretch-blow moulding step.

The hot preform is then taken off and transported into a mould of a blow moulding machine. The transport movement, performed for example by a transfer arm, is coordinated with that of the blow moulding machine, which is generally produced in the form of a rotary carousel that rotates continuously about its vertical axis and carries, on its periphery, a series of identical moulds. Thus, the preform is placed in the mould immediately after it has been opened and the previously formed container has been removed.

The preform is heated beforehand so as to be in the mould at a temperature above the glass transition temperature (about 100° C.) so as to enable it to be formed by stretch-blow moulding. The temperature of the preform at the end of the heating step is slightly above that required inside the mould of the blow moulding machine, so as to take into account the cooling that takes place over the distance that exists between the heating site and the blow-moulding site. Thanks to the simultaneous presence of several moulds, such a blow moulding machine can produce containers at very high rates, of around several tens of thousands of units per hour, i.e. around 1000 to 2000 bottles per hour per mould.

The stretch-blow moulding takes place by stretching using a metal rod and by injecting air at pressures ranging from 3 to 40 bar (3×10⁵ Pa to 4×10⁶ Pa). The air is injected through a nozzle, the end of which is introduced through the opening in the head of the preform.

Bottles manufactured by injecting pressurized air have a relatively satisfactory lifetime. However, the intrinsic properties and characteristics of PET, in particular its specificity which is to crystallize on being stretched, mean that even better results may be envisaged by modifying the container manufacturing process. In particular, it is known that high crystallinity means better mechanical strength.

The present invention makes it possible to extend the average lifetime of the containers within the context of normal transport, distribution and consumption. It also makes it possible to speed up the industrial production process, by optimizing the production steps and minimizing the in-line losses.

The invention applies preferentially to the class of polyesters in general, and to PET in particular.

SUMMARY OF THE INVENTION

The Applicant therefore proposes, within the context presented above, a method of delivering a predetermined volume of beverage into a thermoplastic container formed from a heated preform, the preform being for example approximately cylindrical and positioned in a mould, the method including a step of injecting at least some beverage into a recess in the preform so as to promote expansion of the preform inside the mould, the mould defining the shape of the container, a longitudinal displacement of a stretch rod carried out during a given period ensuring longitudinal elongation of the heated preform, the stretch rod being immobile at the end of the given period, and a volume of beverage greater than 50% of the predetermined volume being present in the recess at said end of the given period.

This method makes it possible to improve the quality of the containers obtained. In general, the condition whereby the bottle-filling piston has already covered more than half of its total travel when the stretching is stopped is a sine qua non condition for preventing the bottle from exploding in the mould.

According to one advantageous feature, a volume of beverage greater than 75%, of the predetermined volume is present in the recess at said end of the given period.

The containers obtained using this method have much better characteristics than those obtained with a conventional stretch-blow moulding method using gaseous fluid to inflate them. In particular, it has been found that, for a given weight and a given type of material, they have a longer lifetime. The degree of crystallinity, i.e. the mass of crystalline phase relative to the mass of polymer, of a container obtained by the method according to the invention may in particular be much higher.

According to one embodiment, the displacement and the injection are controlled by a programmable computer-aided manufacturing device.

Alternatively, and optionally in combination, the displacement and the injection are controlled by a cam.

According to one advantageous feature, during said prior heating step, the temperature of the preform is brought to between 50° C. and 130° C., or even to between 75° C. and 100° C.

Preferably, a speed of the stretch rod reached during said displacement is between 0.5 and 3.0 m/s, or even between 1 and 2.5 m/s.

According to a preferred feature, during the injection step, a volume of beverage has a temperature between 1° C. and 120° C., or even a temperature between 10° C. and 90° C.

Preferentially, provision is made for a longitudinal stretch ratio of the preform, measured between the start and end of the injection step, to be between 2 and 5 or between 2.5 and 4.

Moreover, according to one embodiment, a radial stretch ratio of the preform, measured between the start and end of the injection step, is between 2 and 7, or even between 3 and 4.5.

It should be emphasized that the invention applies most particularly well to the case in which the thermoplastic is chosen from the group consisting of polyethylene terephthalates, polypropylenes, polyethylenes, polycarbonates, polystyrenes, polylactic acids, polyvinyl chlorides and combinations thereof.

Preferably, the method further includes a prior gas injection step so as to promote expansion of said preform, such that the volume of the preform is brought up to a predefined fraction, advantageously 70%, of the predetermined volume.

Advantageously, the prior gas injection step is followed by a beverage injection step so as to promote expansion of said preform until the preform has reached said predetermined volume.

This is because air is not as capable as the beverage of cooling the thermoplastic undergoing expansion. These characteristics therefore have the advantage of providing a more stable method and a wider window in implementing the method.

According to one advantageous feature, the mould is brought beforehand to a temperature at least 50° C. below the melting point of the thermoplastic.

Again, the method according to the invention may also include a subsequent step of fitting a closure cap onto the container.

In this case, the step of injecting at least some of the beverage preferably comprises injecting a volume of beverage into which gas has been introduced beforehand so as to create an overpressure in the neck of the container after the closure cap has been fitted.

Finally, according to one aspect, the longitudinal displacement of the rod is performed at a constant speed.

Also, the invention takes place through a nozzle having a bell-shaped head, so as to reduce the risks of deforming a neck of the preform.

The invention also proposes a device for delivering a predetermined volume of beverage into a thermoplastic container formed from a heated preform, the preform being approximately cylindrical and positioned in a mould, the device comprising means for injecting at least some beverage into a recess in the preform so as to promote expansion of the preform inside the mould, the mould defining the shape of the container, means for longitudinally displacing a stretch rod over a given period and for longitudinally elongating the heated preform, the stretch rod being immobile at the end of the given period, and means for ensuring that a volume of beverage greater than a predefined fraction of the predetermined volume, preferably 50%, is present in the recess at said end of the given period.

Advantageously, this device may include means suitable for carrying out the respective intended steps of the method, taken separately or in combination.

BRIEF DESCRIPTION OF THE DRAWINGS

The invention will now be described in detail with reference to the appended figures, which relate to exemplary embodiments.

FIG. 1 shows the monitoring of the formation of a mineral water bottle according to an example of the prior art.

FIG. 2 shows a crystallinity scale used in relation to the method according to the invention.

FIG. 3 shows a general diagram of the installation used.

FIG. 4 shows the monitoring of the formation of a mineral water bottle according to a preferred embodiment of the invention.

FIG. 5 shows another aspect of the invention.

DETAILED DESCRIPTION OF THE INVENTION

The embodiment given here by way of example relates to a process for manufacturing PET mineral water bottles from a heated preform. The preform has the shape of a cylindrical tube closed at its lower end. The open head of the preform corresponds to the throat or neck of the bottle, onto which a closure cap is screwed.

FIG. 1 shows the variation over time of the position 1 of the stretch rod and of the air pressure 2 in the preform undergoing expansion according to one solution of the prior art.

In this figure, the x-axis represents time, the y-axis on the left represents the linear position of the stretch cam, while the y-axis on the right represents the air pressure in the preform undergoing expansion.

During a first phase 4 of the process, in particular between 50 ms and 275 ms, the stretch rod advances linearly, with an approximately constant speed.

320 ms after the start of the process (reference 3), the stretch rod has reached its final position P_(f), from which it no longer moves.

During a first part 4 a of the first phase of the process, the air pressure 2 in the preform, initially equal to the atmospheric pressure P_(a) and remaining so up to 150 ms after the start of the process, increases up to a value of about 1.4 times the atmospheric pressure, which value is reached 200 ms after the start of the process.

During a second part 4 b of the first phase of the process, lasting a further 100 ms, i.e. up to 300 ms after the start of the process, the pressure remains constant.

During a second phase 5 of the process, the pressure rapidly increases, with an approximately constant rate of rise until 450 ms, when it reaches a value equal to about 8 times the atmospheric pressure.

From this moment on, the pressure in the expanding preform decreases slightly, while still remaining of the order of magnitude of 8 times the atmospheric pressure.

Moreover, and without wishing to be tied down by any scientific theory, it is known that polyester preforms are amorphous and that the stretching induces, at the same time, crystallization and an exothermic reaction. Now, the evolution of heat is deleterious to the development of crystallinity.

Referring to FIG. 2, a first stretch is therefore performed with the stretch rod, causing crystallization and evolution of heat, and at that moment the incompressible fluid is introduced, which then absorbs the heat given off and shifts the equilibrium point of the crystallinity obtained in the final container towards high values, preferably between 30 and 35%.

The crystallinity is measured in a Lloyd-Davenport density column using the following method. The column is filled with a salty (calcium nitrate) solution having a density gradient. The column is calibrated with balls having a known density between 1.335 and 1.455. Next, small pieces of the container according to the invention are immersed in the column and after a certain time these stabilize at a certain height in the column corresponding to a certain density. The measurements are made at 23° C. The table in the figure gives the crystallinity.

Referring to FIG. 3, a stretch rod 10 is inserted into a compressed-air actuator 15. The stretch rod 10 is controlled by a stretch motor which gives it a longitudinal movement (represented by an arrow).

The compressed-air actuator 15 comprises a cylinder 17 controlling an injection head 18, through which the stretch rod 10 passes. The injection head 18 is connected to the neck 20 of a PET preform placed in a mould (not shown), which preform, after being expanded, takes on the shape of a mineral water bottle, this shape being determined by the wall of the mould.

The actuator comprises three chambers, the upper two chambers 15 a and 15 b being filled with compressed air. Between these upper two chambers, a piston wall 19 slides in a direction parallel to the stretch rod (the displacement being represented by an arrow). The stretch rod 10 passes through the centre of this wall 19.

The compressed-air actuator also includes a lateral inlet 30 for the beverage, here mineral water, connected to the third chamber 15 c of the actuator, this being the bottom chamber. The beverage is fed in via a line 32.

An external mineral water inlet feeds the liquid via the remote end of this line 32 into a first valve 34, which is connected to the opening of a single-chamber filling cylinder 40 comprising a piston 42 controlled by a filling motor (movement of which is represented by an arrow). This motor imparts a longitudinal movement on the piston in the single chamber of the filling cylinder 40.

On the line 32 there is a second valve 36, which is in series behind the first valve 34 and the opening of the filling cylinder 40. The line 32 then runs into the bottom chamber 15 c of the compressed-air actuator 15.

The bottom chamber 15 c of the compressed-air actuator is penetrated by the cylinder 17 for controlling the filling head 18, the internal volume of which emerges through the lower outlet of the compressed-air actuator 15 into the filling head 18. The control cylinder has a lateral opening allowing the beverage to circulate between the bottom chamber of the actuator and the inside of the control cylinder.

The stretch rod 10 itself passes through the control cylinder 17 as far as the filling head 18 and the neck 20 of the bottle preform.

FIG. 4 shows the variation over time of the position 101 of the stretch rod and the position 102 of the filling actuator controlling the inflow of the mineral water into the expanded preform.

The horizontal axis represents the time, the left-hand vertical axis represents the position of the stretch rod and the right-hand vertical axis represents the volume of water introduced into the expanded preform, this being proportional to the position of the filling actuator.

During a first part of the process, from 0 to 250 ms, the stretch rod advances at an essentially constant rate, according to a preferred embodiment.

However, according to another embodiment, during a first phase 110 of the process, in particular from 0 to 150 ms, the stretch rod advances at an increasing speed due to a positive acceleration. During a second phase 115 of the process, from 150 ms to 250 ms, the stretch rod advances with a negative acceleration, the speed decreasing until it becomes zero at 250 ms. However, it will be understood that the changes in speed must be sufficiently gentle to ensure regular and reliable stretching of the thermoplastic.

250 ms after the start of the process (reference 103), the stretch rod has reached its final position P_(f), from which it no longer moves.

At the same instant, the filling actuator has introduced a volume V₁ of mineral water into the expanded preform. The volume introduced from the start of the process (therefore between 0 ms and 250 ms) has progressively increased, with a progressive increase in the flow rate (filling actuator displacement acceleration).

During the moments that follow, which constitute a third phase 120 of the process, up to 320 ms, the total volume of water introduced is constant, the flow rate being invariant. Next, the volume suddenly decreases by a small fraction (around 4%) over a period of 40 ms.

From this instant on, the total volume introduced stabilizes around the value V₂, which is finally reached after a few oscillations, the flow rate of liquid being introduced being zero.

A few instants later, starting from 450 ms after the start of the process (reference 104), the filling actuator has reached a final position, from which it no longer moves. At this moment, it has introduced a volume V₂ of mineral water into the expanded preform. The volume V₂ is greater than V₁, but less than twice the volume V₁.

During the method of using the device described, the temperature of the preform is brought beforehand to a value between 50° C. and 130° C., or even between 75° C. and 100° C. In the preferred embodiment, this value is 85° C.

In general, a bottle is defined to be of high quality on the basis of the fact that it has not exploded in the mould.

The tests carried out show that it is not possible to form a bottle completely if physically it has not reached 50% of its final volume at the end of the active stretching.

During the method of using the device described, the temperature of the preform is brought beforehand to a value between 50° C. and 130° C., or even between 75° C. and 100° C. In the preferred embodiment, this value is 95° C., the plastic used being PET.

The rod has a speed of between 0.5 and 3.0 m/s⁻¹, or even between 1.0 and 5 m/s⁻¹. In the preferred embodiment, this value is 1.6 m/s⁻¹.

The temperature of the beverage is brought beforehand to a value between 1° C. and 120° C., preferably between 10° C. and 90° C. In the preferred embodiment, this value is 30° C.

The longitudinal stretch ratio of the thermoplastic is between 2 and 5 or even between 2.5 and 4. In the preferred embodiment, this value is 3.5.

The radial stretch ratio of the thermoplastic is between 2 and 7, or even between 3 and 4.5. In the preferred embodiment, this value is 4.

The thermoplastic is chosen from the group consisting of polyethylene terephthalates, polypropylenes, polyethylenes, polycarbonates, polystyrenes, polylactic acids, polyvinyl chlorides and combinations thereof. In the preferred embodiment, it is PET.

The temperature of the mould is at least 50° C. below the melting point of the thermoplastic, which in the case of PET is 230° C. Preferably, this temperature is maintained below 100° C. In the preferred embodiment, the temperature of the mould is equal to the ambient temperature.

Referring to FIG. 5, a bell-shaped nozzle end-piece 500 according to a preferred embodiment is shown. The internal and external pressures on either side of the circumference of the neck of the preform (i.e. on the external surfaces 510 of the neck and on the internal surfaces 520 of the neck) are identical, owing to the presence of a passage 505 connecting the volumes on either side of the circumference, inside the nozzle. During filling, sealing is provided by the flange 530 on the preform. Thanks to this device, there is no risk of the neck of the preform deforming while a pressurized fluid is being injected by the nozzle.

According to another embodiment, a nozzle end-piece holds the external surfaces 510 of the neck of the preform in such a way that when a pressurized fluid is injected via the top of the nozzle into the recess of the preform, the pressure exerted on the internal walls 520 of the neck of the preform by the fluid is compensated for by the holding by the walls of the bell-shaped nozzle end-piece. The neck of the preform therefore does not deform, despite the high pressure.

Of course, the invention is not limited to the embodiments described and illustrated by the appended drawings; rather it extends to all variants that can be envisaged by a person skilled in the art within the scope of the claims. 

The invention claimed is:
 1. Method of delivering a predetermined volume of beverage into a thermoplastic container formed from a heated preform, the preform being positioned in a mold, comprising the steps of injecting at least some beverage into a recess in the preform so as to promote expansion of the preform inside the mold, the mold defining the shape of the container, a longitudinal displacement of a stretch rod during a given period ensures a longitudinal elongation of the heated preform, the stretch rod being immobile at the end of the given period, and a volume of beverage greater than 50% of the predetermined volume being present in the recess at the end of the given period.
 2. Method according to claim 1, wherein during a prior heating step, the temperature of the preform is between 50° C. and 130° C.
 3. Method according to claim 2, wherein during the prior heating step, the temperature of the preform is between 75° C. and 100° C.
 4. Method according to claim 1, wherein a speed of the stretch rod reached during the displacement is between 0.5 and 3.0 m/s.
 5. Method according to claim 1, wherein a speed of the stretch rod reached during the displacement is between 1 and 2.5 m/s.
 6. Method according to claim 1, wherein during the injection step, a volume of beverage has a temperature between 1° C. and 120° C.
 7. Method according to claim 6, wherein during the injection step, a volume of beverage has a temperature of between 10° C. and 90° C.
 8. Method according to claim 1, wherein a longitudinal stretch ratio of the preform, measured between the start and end of the injection step, is between 2 and
 5. 9. Method according to claim 8, wherein a longitudinal stretch ratio of the preform, measured between the start and end of the injection step, is between 2.5 and
 4. 10. Method according to claim 1, wherein a radial stretch ratio of the preform, measured between the start and end of the injection step, is between 2 and
 7. 11. Method according to claim 1, wherein a radial stretch ratio of the preform, measured between the start and end of the injection step, is between 3 and 4.5.
 12. Method according to claim 1, wherein the thermoplastic is selected from the group consisting of polyethylene terephthalates, polypropylenes, polyethylenes, polycarbonates, polystyrenes, polylactic acids, polyvinyl chlorides and combinations thereof.
 13. Method according to claim 1, comprising the step of injecting gas so as to promote expansion of the preform such that the volume of the preform is brought up to a predefined fraction of the predetermined volume.
 14. Method according to claim 13, wherein the predefined fraction is equal to 70% of the predetermined volume.
 15. Method according to claim 13, wherein the gas injection step is followed by a beverage injection step so as to promote expansion of the preform until the preform has reached the predetermined volume.
 16. Method according to claim 1, wherein the mold is brought beforehand to a temperature at least 50° C. below the melting point of the thermoplastic.
 17. Method according to claim 1, wherein the longitudinal displacement of the rod is performed at a constant speed.
 18. Method according to claim 1, wherein the injection takes place through a nozzle having a head configured to reduce the risks of deforming a neck of the preform. 